Microstructure and high temperature reciprocating sliding wear properties of MoSi2/TiC/γ-Ni composite coating in-situ synthesized by co-axial powder feeding plasma transferred arc cladding.
【作者单位】1 Materials Science and Engineering Research Center, Beijing Jiaotong University, Beijing, 100044, PR China 2 School of Science, Tibet University, Lhasa, 850000, PR China 3 Semiconductor Manufacturing International (Beijing) Corporation, 100176, PR China
【摘要】 A MoSi 2 /TiC/γ-Ni high temperature wear-resistant composite coating was in-situ synthesized on AISI 321 substrate by co-axial powder feeding plasma transferred arc cladding process using powders blend of Ni, Ti, Mo, Si and Ni-P coated graphite as r...